Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment

	Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment
Department	固体润滑国家重点实验室（LSL）
	Zhu Yuhua ; Liu Hao ; Zhang Dongyue ; Wang Jianzhang; Yan Fengyuan
The second department	聚合物摩擦学组
	2022
Source Publication	Tribology International
Volume	168 Issue:107445 Pages:1-9
Abstract	Monel 400 alloy is widely used in marine engineering due to its corrosion resistance. In this study, the tribo- corrosion behavior of Monel 400 alloy has been investigated under cathodic and anodic polarization conditions. The results revealed that the material loss increased under both cathodic and anodic polarization, while the damage mechanism varied. Under cathodic polarization condition, the damage is caused by delamination of the worn surface and crack propagation in the subsurface, which gets more seriously at more negative polarization values. Under higher anodic polarization values, the lubricating performance of in-situ generated corrosion product was weakened. As the anodic polarization value increased, the diameter of corrosion products increased and got easier to be sheared-off during the sliding process.
Keyword	Corrosive Wear Sliding Delamination
Indexed By	SCI
If	5.62
Language	英语
compositor	第一作者单位
Document Type	期刊论文
Identifier	http://ir.licp.cn/handle/362003/29609
Collection	固体润滑国家重点实验室（LSL）
Corresponding Author	Wang Jianzhang
Affiliation	1.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences 2.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences 3.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences 4.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences 5.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences
Recommended Citation GB/T 7714	Zhu Yuhua,Liu Hao,Zhang Dongyue,et al. Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment[J]. Tribology International,2022,168(107445):1-9.
APA	Zhu Yuhua,Liu Hao,Zhang Dongyue,Wang Jianzhang,&Yan Fengyuan.(2022).Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment.Tribology International,168(107445),1-9.
MLA	Zhu Yuhua,et al."Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment".Tribology International 168.107445(2022):1-9.

Files in This Item:
File Name/Size	DocType	Version	Access	License
Effect of polarizati（8189KB）	期刊论文	作者接受稿	开放获取	CC BY-NC-SA	View Application Full Text

File name:	Effect of polarization potentials on tribocorrosion behavior of Monel 400 alloy in seawater environment.pdf
Format:	Adobe PDF

If you have any objections to this item, please fill out the form below and the administrator will contact you as soon as possible.
Content:
Email：	*
Institution:
Verification Code:	Refresh

Any comments and suggestions are welcomed.
Title:	*
Content:
Email：	*
Verification Code:	Refresh

固体润滑国家重点实验室（LSL）知识库