Al matrix composites reinforced with Ti₃AlC₂ and Cu coated Ti₃AlC₂ were prepared by hot-press sintering approach. It was confirmed that Ti₃AlC₂ displayed poor wettability with Al, resulting in the poor interfacial bonding strength between Ti₃AlC₂ and Al matrix. However, Al₂Cu layer could be formed due to the reaction between Cu and Al during the sintering process, when Cu coated Ti₃AlC₂ was incorporated in Al matrix. Because of the formation of enhanced Al₂Cu interface, the mechanical and tribological properties were significantly improved. The Al₂Cu layer could bridge Ti₃AlC₂ particle and Al matrix effectively, which contributed to absorbing energy when load was applied, to provide better mechanical properties. Moreover, Ti₃AlC₂ particle could exhibit powerful pinning effect to inhibit two-body abrasion and adhesion wear, which was favorable for forming smooth tribo-oxidation surface to yield low friction coefficient. The wear mechanism was believed to be oxidation and fatigue wear.